The best products for mattresses and upholstery
We have different adhesives for mattrresses: solvent based, water based and hot-melt.
SOLVENT BASED ADHESIVES
PRACTICALLY IMMEDIATE DRYING (FEW SECONDS)
EXCELLENT INITIAL TACK
HIGH OPEN TIME
SIMPLICITY IN APPLICATION EQUIPMENT
This type of adhesive is characterized by being useful on all mattress surfaces. Presented in bottles, drums and containers, it can be applied unilaterally and bilaterally to both high and low separation tension supports.
Its viscosity is suitable for spray application (100 – 500 cPs) and its excellent open time gives it great versatility (from a few minutes to several hours).
This type of adhesive is excellent wet on foams and has high flexibility. Its high initial adhesion occurs immediately after application and does not require drying.
| PRODUCT | VISCOSITY (20 ºC MPA.S) | BASE | FEATURES |
|---|---|---|---|
| TELCOFOAM 5056 | 100 | RUBBER IN DISSOLUTION | General application |
| TELCOFOAM 5056-R | 100 | RUBBER IN DISSOLUTION | General application, higher temperature resistance than the 5056 |
| TELCOFOAM 5324 | 500 | RUBBER IN DISSOLUTION | Very high in solids content, less solvent use |
| TELCOFOAM 5025 | 120 | RUBBER IN DISSOLUTION | High content in solids , less solvent use |
| OBRADOR 702 | 250 | POLYCHLOROPRENE IN DISSOLUTION | Wide range use, Long open time |
| OBRADOR 662 | 260 | POLYCHLOROPRENE IN DISSOLUTION | Wide range use, high temperature resistance |
WATER BASED ADHESIVES
VOC REDUCTION
LESS ENVIRONMENTAL DAMAGE
NOT FLAMMABLE
HIGH TEMPERATURES RESISTANCE
INSURANCE COST REDUCTION
This type of adhesive is compatible with the gluing of all surfaces in the mattress industry. It comes packaged in a bottle, container and Bag in Box.
Its application is bilateral, being applicable to glued supports with low separation tension. On the other hand, its viscosity is suitable for spray application: 100 – 1000 cPs.
It has an open time of 5-10 minutes, being excellent wet on foams. In addition, it has high flexibility and its high initial adhesion, immediately after application, does not require drying.
| PRODUCT | VISCOSITY (20 ºC MPA.S) | BASE | FEATURES |
|---|---|---|---|
| OBRATEX 5302 C | 100 | SYNTHETIC RUBBER (WATER BASED) | Wide range use. Bicomponent |
| CATALIZADOR 5302 | ———– | ORGANIC SOLUTION (WATER BASED) | Additive for OBRATEX 5302 C |
| OBRATEX 5321 | 600 | SYNTHETIC RUBBER (WATER BASED) | Wide range use. Monocomponent |
HOT-MELT ADHESIVES
100% SOLID
VERY FAST SET SPEED (FEW SECONDS)
IMMEDIATELY MATTRESS MANUFACTURING PROCESS
HIGH RESISTANCE UNDER ENVIRONMENTAL CONDITIONS
AVOID ODOURS AND HUMIDITY
Useful for gluing all surfaces in the mattress sector, it comes packaged in tablets, pillow and ecobock.
It is for unilateral application on supports glued with high and low separation tension, either by spray, roller, injection or spiral.
Its open time provides great versatility (from a few seconds to self-adhesive with infinite tack).
It works excellent wet on foams, in addition to having great flexibility and high initial adhesion (immediately after application without drying).
| PRODUCT | PACKAGING | COLOUR | VISCOSITY (160 ºC) | OPEN TIME (160 ºC) |
|---|---|---|---|---|
| HOT-MELT PSA (PRESSURE SENSITIVE) | ||||
| PRODAS 2114 | ECOBLOCK | AMBER | 2800 mPa.s | 12 sec (law tack residual) |
| HOTMELT NO PSA WITHOUT VELCRO EFFECT | ||||
| PRODAS 2282 | ECOBLOCK | PALE AMBER | 4220 mPa.s | 18 sec |
| PRODAS 2037 | ECOBLOCK | WHITE | 3250 mPa.s | 19 sec |